Physical and mechanical properties of grades for cemented carbide inserts &
Brazed Tips and their applications recommended
| |||||
ISO
Code
|
Grade
|
Physical and mechanical
properties
|
Applications recommended
| ||
Density
g/cm ³
|
Hardness
HRA
|
TRS
Mpa
| |||
P10
|
YT05
|
12.6
|
92.5
|
1260
|
It is suitable for finishing of steel and casting
steel machining,high cutting speed,small feed
rate and low depth is recommended.
|
YT15
|
11.3
|
91
|
1300
|
It is suitable for semi-finishing of steel and
casting steel machining,high cutting speed ,
medium feed rate is recommended.
| |
P20
|
YC201
|
11.79
|
91.8
|
1400
|
It is suitable for semi-finishing and light
roughing machining of steel,casting steel
and stainless steel.it is a suitable grade
for a wide application.
|
YT14
|
11.4
|
90.5
|
1400
|
It is suitable for semi-finishing of steel and
casting steel.
| |
YS25
|
13.0
|
90.5
|
1780
|
It is used for milling machining of steel and
casting steel.
| |
P30
|
YT5
|
12.8
|
89.5
|
1570
|
Suitable for the heavy duty rough turning or
steel and cast steel with a big feed rate at a
medium and low speed under unfavorable
working conditions.
|
P40
|
YC45
|
12.75
|
90
|
2250
|
Suitable for the heavy duty turning of steel
and cast steel with a big feed rate and also
for face milling.
|
M05
|
YS8
|
13.9
|
92.5
|
1720
|
It can be used for the finishing of iron based
and nickel based high-temperature alloys
and high-strength steel and it can also be
used for the finishing of chilled cast iron,
heat resistant stainless steel,high manganese
steel and hardening steel.
|
M10
|
YW3
|
12.9
|
92
|
1390
|
Suitable for the finishing and semi-finishing
of stainless steel and conventional alloy steel.
|
M10
|
YW1
|
13
|
91.5
|
1290
|
It is suitable for semi-finishing of stainless
steel and general alloy steel machining.
|
M20
|
YM201
|
13.9
|
93
|
1600
|
It is suitable for semi-finishing of Fe,Ni high
temperature alloy,cold hard cast irons,
stainless steel with good heat-resistance
and nonferrous metal.it is a wide application.
|
M20
|
YS2T
|
14.4
|
91.5
|
1960
|
It is suitable for finishing and semi –finishing
of stainless steel,alloy steel,Fe alloy.
|
M20
|
YW2
|
12.9
|
90.5
|
1460
|
It is suitable for semi-finishing and light
roughing of stainless steel and alloy steel.
|
K05
|
YG3X
|
15.1
|
91.5
|
1300
|
It is suitable for finishing of casting iron,
nonferrous metal,heat-resistance alloy
and Ti alloy.
|
K05
|
YG3
|
15.0
|
90.5
|
1300
|
It is suitable for semi-finishing of casting iron,
nonferrous metal,heat-resistance alloy and
Ti alloy.
|
K10
|
YM201
|
13.9
|
93.0
|
1600
|
It is suitable for semi-finishing of Fe,Ni high
temperature alloy,cold hard cast irons,
stainless steel with good heat-resistance
and nonferrous metal.it is a wide application.
|
K10
|
YG6X
|
14.8
|
91
|
1560
|
It is suitable for semi-finishing to light roughing
of casting iron,nonferrous metal,
heat-resistance alloy and Ti alloy.
|
K20
|
YD201
|
14.89
|
91.0
|
1800
|
It is suitable for roughing to finishing machining
of heat-resistance alloy,Ti alloy,casting iron
and aluminum alloy.
|
K20
|
YG6
|
14.9
|
89.5
|
1670
|
It is suitable for light roughing and
semi-finishing of casting iron,nonferrous metal,
heat-resistance alloy and Ti alloy.
|
K20
|
YG8
|
14.6
|
89
|
1840
|
It is suitable for semi-finishing and roughing
of casting iron,nonferrous metal,
heat-resistance alloy and Ti alloy at
continuous and intermittent machining
conditions.
|